Uh List admin? We have a problem!


At 06:41 PM 7/18/2011, you wrote:


>Reminder from:   <http://groups.yahoo.com/group/locost/cal>locost Yahoo! Group
>
>Title:   Auto insurance, reduce costs but maintain protection
>
>Date:   Tuesday July 19, 2011
>Time:   10:00 am - 11:00 am
>Repeats:   This event repeats every day.

Pat Patterson
Abbotsford, BC, Canada


2001 PT Cruiser
83 450 Honda Nighthawk
78 F350    460/C6 on propane
71 Bronco 302/C4/D20 D44/9"


Some people try to turn back their odometers.  Not me, I want people
to know "why" I look this way.  I've traveled a long way and some of
the roads weren't paved.

"If you can't take the heat, don't tickle the dragon."














[Non-text portions of this message have been removed]

Yep, and not just on this group either, it seams to be a growing
problem. On one other group i'm with the owner sent out an email to all
the members asking for a reply to his email and those that didn't reply
have been cut from the group. Haven't had anymore spam on the group for
about two months or so now.

Rob

On 19/07/2011 2:04 PM, Pat Patterson wrote:
>
> Uh List admin? We have a problem!
>
> At 06:41 PM 7/18/2011, you wrote:
>
> >Reminder from: <http://groups.yahoo.com/group/locost/cal>locost
> Yahoo! Group
> >
> >Title: Auto insurance, reduce costs but maintain protection
> >
> >Date: Tuesday July 19, 2011
> >Time: 10:00 am - 11:00 am
> >Repeats: This event repeats every day.
>
> Pat Patterson
> Abbotsford, BC, Canada
>
> 2001 PT Cruiser
> 83 450 Honda Nighthawk
> 78 F350 460/C6 on propane
> 71 Bronco 302/C4/D20 D44/9"
>
> Some people try to turn back their odometers. Not me, I want people
> to know "why" I look this way. I've traveled a long way and some of
> the roads weren't paved.
>
> "If you can't take the heat, don't tickle the dragon."
>
> [Non-text portions of this message have been removed]
>
>



[Non-text portions of this message have been removed]

Log onto the list website. Open the calender pick the tasks tab (or
the one next to it)
It will show a list click show all, click the check all and then
delete. It will say they are about 9 repeating items
but will clean this out. Otherwise you will get these every friggin
day as long as you are on the list.

It should also show the name of the twit who did it. I just killed it
before looking. Was going to unsubscribble.

Perhaps Mr Mod could turn off some of the available options ;-]

Dave

At 09:04 PM 18/07/2011, you wrote:
>Uh List admin? We have a problem!
>
>
>At 06:41 PM 7/18/2011, you wrote:
>
>
> >Reminder from:   <http://groups.yahoo.com/group/locost/cal>locost
> Yahoo! Group
> >
> >Title:   Auto insurance, reduce costs but maintain protection
> >
> >Date:   Tuesday July 19, 2011
> >Time:   10:00 am - 11:00 am
> >Repeats:   This event repeats every day.
>
>Pat Patterson
>Abbotsford, BC, Canada
>
>
>2001 PT Cruiser
>83 450 Honda Nighthawk
>78 F350    460/C6 on propane
>71 Bronco 302/C4/D20 D44/9"
>
>
>Some people try to turn back their odometers.  Not me, I want people
>to know "why" I look this way.  I've traveled a long way and some of
>the roads weren't paved.
>
>"If you can't take the heat, don't tickle the dragon."
>
>
>
>
>
>
>
>
>
>
>
>
>
>
>[Non-text portions of this message have been removed]
>
>
>
>------------------------------------
>
>Yahoo! Groups Links
>
>
>

[Non-text portions of this message have been removed]

I checked the tasks as soon as I saw the problem, but I think Yahoo beat me to
it - no repeating tasks.

Not sure how it was done, beats me why they think it worthwhile.

James, Mod.

--- In locost@yahoogroups.com, Wragie <wragie@...> wrote:
>
> Log onto the list website. Open the calender pick the tasks tab (or
> the one next to it)
> It will show a list click show all, click the check all and then
> delete. It will say they are about 9 repeating items
> but will clean this out. Otherwise you will get these every friggin
> day as long as you are on the list.
>
> It should also show the name of the twit who did it. I just killed it
> before looking. Was going to unsubscribble.
>
> Perhaps Mr Mod could turn off some of the available options ;-]
>
> Dave
>
> At 09:04 PM 18/07/2011, you wrote:
> >Uh List admin? We have a problem!
> >
> >
> >At 06:41 PM 7/18/2011, you wrote:
> >
> >
> > >Reminder from:   <http://groups.yahoo.com/group/locost/cal>locost
> > Yahoo! Group
> > >
> > >Title:   Auto insurance, reduce costs but maintain protection
> > >
> > >Date:   Tuesday July 19, 2011
> > >Time:   10:00 am - 11:00 am
> > >Repeats:   This event repeats every day.
> >
> >Pat Patterson
> >Abbotsford, BC, Canada
> >
> >
> >2001 PT Cruiser
> >83 450 Honda Nighthawk
> >78 F350    460/C6 on propane
> >71 Bronco 302/C4/D20 D44/9"
> >
> >
> >Some people try to turn back their odometers.  Not me, I want people
> >to know "why" I look this way.  I've traveled a long way and some of
> >the roads weren't paved.
> >
> >"If you can't take the heat, don't tickle the dragon."
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >[Non-text portions of this message have been removed]
> >
> >
> >
> >------------------------------------
> >
> >Yahoo! Groups Links
> >
> >
> >
>
> [Non-text portions of this message have been removed]
>

*
*




*may i be excused Dear friend, How are you doing? I find a site to sell
electronic products with very good price. Laptop, DC and Cellphone even
Motorcycle are very popular. Their products are original quality with very
low price as wholesale business supplier. They also can do retail business
for end user now. Maybe it is fit for your business . If you like you can
contact them : www.eleblc.com   Millions of kisses and good wishes!! *


[Non-text portions of this message have been removed]

Hello Locost/Lotus builders! I've been reading this group during some years, and
finally, as I've started cutting the tubes, getting all the inferior rails
(using pat prince scans as the reference and Autocad for neatness) cut and
straight for welding, I would like to have your advice in the joining technique.
The thing is; I have an oxyacetilene torch, and no MIG, nor TIG, no 220v either.
Does it worth the effort to get the tubes into a shop to Tack weld them with
MIG, then braze it with nickel bronze at home???? mainly, i'm concerned with the
lack of proper jigs for brazing it from the start, keeping it straight during
the brazing (Being a complete practical novice on it, some literature already
seen) so, i thought of the MIG for tacking all, four corners by tube prior to
brazing.

Another concern is the time involved, I am doing this project as slow as my work
allows it, so if I have the chassis at home, tacked, it could be brazed little
by little.

And third!! this would be in the brazing alternative. Three tubes, two of them
joint by their extremes, the third standing in it extreme, half of the inch on
one tube, half on the other. Should I braze First the two underling tubes, THEN
the standing one?. Should I Tack the three together, then braze the whole "Tee"
Thing???

Anyway, all of this is speculative, because until now, The hack saw and lathe
back grinder have been the tools used. It would be very good for me
(fundamental) to have your ideas on it

Kind regards and happy car-making!

D.R.

Where are you from? English is obviously not your language. I'm
hoping something is being lost in translation because I wouldn't
braze any of the joints. I'd be willing to weld them with
oxyacetylene but not braze.

Knowing your language and location might help someone close to you
translate and or help with welding.

At 07:03 PM 8/20/2011, you wrote:
>
>
>Hello Locost/Lotus builders! I've been reading this group during
>some years, and finally, as I've started cutting the tubes, getting
>all the inferior rails (using pat prince scans as the reference and
>Autocad for neatness) cut and straight for welding, I would like to
>have your advice in the joining technique. The thing is; I have an
>oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
>worth the effort to get the tubes into a shop to Tack weld them with
>MIG, then braze it with nickel bronze at home???? mainly, i'm
>concerned with the lack of proper jigs for brazing it from the
>start, keeping it straight during the brazing (Being a complete
>practical novice on it, some literature already seen) so, i thought
>of the MIG for tacking all, four corners by tube prior to brazing.
>
>Another concern is the time involved, I am doing this project as
>slow as my work allows it, so if I have the chassis at home, tacked,
>it could be brazed little by little.
>
>And third!! this would be in the brazing alternative. Three tubes,
>two of them joint by their extremes, the third standing in it
>extreme, half of the inch on one tube, half on the other. Should I
>braze First the two underling tubes, THEN the standing one?. Should
>I Tack the three together, then braze the whole "Tee" Thing???
>
>Anyway, all of this is speculative, because until now, The hack saw
>and lathe back grinder have been the tools used. It would be very
>good for me (fundamental) to have your ideas on it
>
>Kind regards and happy car-making!
>
>D.R.

Pat Patterson
Abbotsford, BC, Canada


2001 PT Cruiser
83 450 Honda Nighthawk
78 F350    460/C6 on propane
71 Bronco 302/C4/D20 D44/9"


Some people try to turn back their odometers.  Not me, I want people
to know "why" I look this way.  I've traveled a long way and some of
the roads weren't paved.

"If you can't take the heat, don't tickle the dragon."

Daniel, If you have oxy acetylene you don't need anything else. You will
need 00, 0, 1, and 2 size torches to cover all the thicknesses of tubing and
tabs. Add a cutting torch for fast fabrication of suspension tabs and you
have everything you need. It may take a little longer, but you can fit,
tack, check alignment, and finish weld and you'll be fine. Add a rosebud
torch, you also have the advantage of being able to do bending, which
neither MIG nor TIG will give you.
Brazing requires very precise fits, welding is much more lenient. Just use
good quality welding rod, ER70S6 is very common. no scrap wire or hangers
:-}, that will cause cracks down the road.
There are many videos out there showing oxy acetylene welding of aircraft
fuselages, engine mounts, and control surfaces, get one of those and
practice, practice, practice. Make sample welds on some tube drops, cut
through them at a right angle and take those to a welder when you think you
are skilled enough and ready to start you chassis. He will be able to give
you an honest appraisal or your  skill.
Almost every aircraft built during World War II had steel parts that
were oxy acetylene welded. From the Spitfire to the Super Fortress, they had
major structural weldments that were oxy acetylene welded. You will find you
have more control of weld size and a much easier time getting into tight
corners than with a MIG.
Good luck.

Rick Girard


On Sat, Aug 20, 2011 at 9:03 PM, Daniel <drichardson_ve@...> wrote:

> **
>
>
> Hello Locost/Lotus builders! I've been reading this group during some
> years, and finally, as I've started cutting the tubes, getting all the
> inferior rails (using pat prince scans as the reference and Autocad for
> neatness) cut and straight for welding, I would like to have your advice in
> the joining technique. The thing is; I have an oxyacetilene torch, and no
> MIG, nor TIG, no 220v either. Does it worth the effort to get the tubes into
> a shop to Tack weld them with MIG, then braze it with nickel bronze at
> home???? mainly, i'm concerned with the lack of proper jigs for brazing it
> from the start, keeping it straight during the brazing (Being a complete
> practical novice on it, some literature already seen) so, i thought of the
> MIG for tacking all, four corners by tube prior to brazing.
>
> Another concern is the time involved, I am doing this project as slow as my
> work allows it, so if I have the chassis at home, tacked, it could be brazed
> little by little.
>
> And third!! this would be in the brazing alternative. Three tubes, two of
> them joint by their extremes, the third standing in it extreme, half of the
> inch on one tube, half on the other. Should I braze First the two underling
> tubes, THEN the standing one?. Should I Tack the three together, then braze
> the whole "Tee" Thing???
>
> Anyway, all of this is speculative, because until now, The hack saw and
> lathe back grinder have been the tools used. It would be very good for me
> (fundamental) to have your ideas on it
>
> Kind regards and happy car-making!
>
> D.R.
>
>
>


[Non-text portions of this message have been removed]

Daniel,



Hoood on there. I have a decade of brazing experience (mostly Chrome Molly
and Remolds steel) special tubing and yes, you could braze an entire Lotcost
frame, but the tight tolerances needed to make proper fillets would take WAY
too much time and energy and add very little value. The think walled
rectangular tubes are mostly "clean cut" with very few compound cuts for the
chassis. but brazing or for that matter any O2AC gas flam mending applies a
LOT of heat that will temper the joints.  The ideal fusion should be at
least a MIG and if you are as budget constrained as I am, you can typically
pick-up a used MIG and forgo the gas (Flux weld works hotter, and has more
slag - but no additional GAS cylinders to refill) I am reluctant to
recommend this, but I have seen Harbor Freight MIG welders for a few hundred
dollars.  However I would look for a Lincoln or Miller / Hobart and the
small "lunchbox" models often has 110 v power source, but your duty-cycle is
10-20% no big deal, as you are also using thin walled tube.



If I were to braze a chassis together then I would chose to use .120 wall
round tube.  Heavier and stronger than typical Locost but the effort you
will be outing into it would at least show the results and justify the time.
(Just get a MIG. you will be very glad you did!)



~John



From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
Daniel
Sent: Saturday, August 20, 2011 7:04 PM
To: locost@yahoogroups.com
Subject: [locost] Question on Brazing





Hello Locost/Lotus builders! I've been reading this group during some years,
and finally, as I've started cutting the tubes, getting all the inferior
rails (using pat prince scans as the reference and Autocad for neatness) cut
and straight for welding, I would like to have your advice in the joining
technique. The thing is; I have an oxyacetilene torch, and no MIG, nor TIG,
no 220v either. Does it worth the effort to get the tubes into a shop to
Tack weld them with MIG, then braze it with nickel bronze at home????
mainly, i'm concerned with the lack of proper jigs for brazing it from the
start, keeping it straight during the brazing (Being a complete practical
novice on it, some literature already seen) so, i thought of the MIG for
tacking all, four corners by tube prior to brazing.

Another concern is the time involved, I am doing this project as slow as my
work allows it, so if I have the chassis at home, tacked, it could be brazed
little by little.

And third!! this would be in the brazing alternative. Three tubes, two of
them joint by their extremes, the third standing in it extreme, half of the
inch on one tube, half on the other. Should I braze First the two underling
tubes, THEN the standing one?. Should I Tack the three together, then braze
the whole "Tee" Thing???

Anyway, all of this is speculative, because until now, The hack saw and
lathe back grinder have been the tools used. It would be very good for me
(fundamental) to have your ideas on it

Kind regards and happy car-making!

D.R.





[Non-text portions of this message have been removed]

Daniel

I have built one using Mig and I've done brazing using liquid in line flux which
is good if your joints are perfect but for a Locost built in a lockup I agree
with John get a Mig it just makes sense.
Mine took 2 years to build and the fastest part was the chassis. The devil is in
the detail my friend get the chassis done and you will only be 20% there if
that.

Good luck with your build.

Dougie

Sent from my iPhone

On 22 Aug 2011, at 22:43, "John Saguto" <John@...> wrote:

> Daniel,
>
> Hoood on there. I have a decade of brazing experience (mostly Chrome Molly
> and Remolds steel) special tubing and yes, you could braze an entire Lotcost
> frame, but the tight tolerances needed to make proper fillets would take WAY
> too much time and energy and add very little value. The think walled
> rectangular tubes are mostly "clean cut" with very few compound cuts for the
> chassis. but brazing or for that matter any O2AC gas flam mending applies a
> LOT of heat that will temper the joints. The ideal fusion should be at
> least a MIG and if you are as budget constrained as I am, you can typically
> pick-up a used MIG and forgo the gas (Flux weld works hotter, and has more
> slag - but no additional GAS cylinders to refill) I am reluctant to
> recommend this, but I have seen Harbor Freight MIG welders for a few hundred
> dollars. However I would look for a Lincoln or Miller / Hobart and the
> small "lunchbox" models often has 110 v power source, but your duty-cycle is
> 10-20% no big deal, as you are also using thin walled tube.
>
> If I were to braze a chassis together then I would chose to use .120 wall
> round tube. Heavier and stronger than typical Locost but the effort you
> will be outing into it would at least show the results and justify the time.
> (Just get a MIG. you will be very glad you did!)
>
> ~John
>
> From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
> Daniel
> Sent: Saturday, August 20, 2011 7:04 PM
> To: locost@yahoogroups.com
> Subject: [locost] Question on Brazing
>
> Hello Locost/Lotus builders! I've been reading this group during some years,
> and finally, as I've started cutting the tubes, getting all the inferior
> rails (using pat prince scans as the reference and Autocad for neatness) cut
> and straight for welding, I would like to have your advice in the joining
> technique. The thing is; I have an oxyacetilene torch, and no MIG, nor TIG,
> no 220v either. Does it worth the effort to get the tubes into a shop to
> Tack weld them with MIG, then braze it with nickel bronze at home????
> mainly, i'm concerned with the lack of proper jigs for brazing it from the
> start, keeping it straight during the brazing (Being a complete practical
> novice on it, some literature already seen) so, i thought of the MIG for
> tacking all, four corners by tube prior to brazing.
>
> Another concern is the time involved, I am doing this project as slow as my
> work allows it, so if I have the chassis at home, tacked, it could be brazed
> little by little.
>
> And third!! this would be in the brazing alternative. Three tubes, two of
> them joint by their extremes, the third standing in it extreme, half of the
> inch on one tube, half on the other. Should I braze First the two underling
> tubes, THEN the standing one?. Should I Tack the three together, then braze
> the whole "Tee" Thing???
>
> Anyway, all of this is speculative, because until now, The hack saw and
> lathe back grinder have been the tools used. It would be very good for me
> (fundamental) to have your ideas on it
>
> Kind regards and happy car-making!
>
> D.R.
>
> [Non-text portions of this message have been removed]
>
>
>
>
> Click here to report this email as spam.
>


This message has been scanned for malware by SurfControl plc.
www.surfcontrol.com


[Non-text portions of this message have been removed]

Dan,
I brazed 90 % of my frame with some high tensile strength 130K psi rod, the kind
that is used to attach tool bits to a tool bar. I had never welded before or
brazed, read up on it and made a lot of test pieces that I pounded apart with a
BMFH. Did that until I was satisfied with my progress enough to put my bones
into a "crate like that". I have not seen any weakening of any of the joints or
failures. The brazing rod was $8 / lb. in 1983, I'm sure that it is a lot more
now.
Esko

----- Original Message -----
From: "John Saguto" <John@...>
To: locost@yahoogroups.com
Sent: Monday, August 22, 2011 2:13:14 PM
Subject: RE: [locost] Question on Brazing






Daniel,

Hoood on there. I have a decade of brazing experience (mostly Chrome Molly
and Remolds steel) special tubing and yes, you could braze an entire Lotcost
frame, but the tight tolerances needed to make proper fillets would take WAY
too much time and energy and add very little value. The think walled
rectangular tubes are mostly "clean cut" with very few compound cuts for the
chassis. but brazing or for that matter any O2AC gas flam mending applies a
LOT of heat that will temper the joints. The ideal fusion should be at
least a MIG and if you are as budget constrained as I am, you can typically
pick-up a used MIG and forgo the gas (Flux weld works hotter, and has more
slag - but no additional GAS cylinders to refill) I am reluctant to
recommend this, but I have seen Harbor Freight MIG welders for a few hundred
dollars. However I would look for a Lincoln or Miller / Hobart and the
small "lunchbox" models often has 110 v power source, but your duty-cycle is
10-20% no big deal, as you are also using thin walled tube.

If I were to braze a chassis together then I would chose to use .120 wall
round tube. Heavier and stronger than typical Locost but the effort you
will be outing into it would at least show the results and justify the time.
(Just get a MIG. you will be very glad you did!)

~John




[Non-text portions of this message have been removed]

Pat,

Why would you not braze the frame together? All the Lotus 7 frames were
brazed and the non-metric Caterham frames are still brazed, so what gives?

Esko



From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
Pat Patterson
Sent: Monday, August 22, 2011 7:41 AM
To: locost@yahoogroups.com
Subject: Re: [locost] Question on Brazing





Where are you from? English is obviously not your language. I'm
hoping something is being lost in translation because I wouldn't
braze any of the joints. I'd be willing to weld them with
oxyacetylene but not braze.

Knowing your language and location might help someone close to you
translate and or help with welding.

At 07:03 PM 8/20/2011, you wrote:
>
>
>Hello Locost/Lotus builders! I've been reading this group during
>some years, and finally, as I've started cutting the tubes, getting
>all the inferior rails (using pat prince scans as the reference and
>Autocad for neatness) cut and straight for welding, I would like to
>have your advice in the joining technique. The thing is; I have an
>oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
>worth the effort to get the tubes into a shop to Tack weld them with
>MIG, then braze it with nickel bronze at home???? mainly, i'm
>concerned with the lack of proper jigs for brazing it from the
>start, keeping it straight during the brazing (Being a complete
>practical novice on it, some literature already seen) so, i thought
>of the MIG for tacking all, four corners by tube prior to brazing.
>
>Another concern is the time involved, I am doing this project as
>slow as my work allows it, so if I have the chassis at home, tacked,
>it could be brazed little by little.
>
>And third!! this would be in the brazing alternative. Three tubes,
>two of them joint by their extremes, the third standing in it
>extreme, half of the inch on one tube, half on the other. Should I
>braze First the two underling tubes, THEN the standing one?. Should
>I Tack the three together, then braze the whole "Tee" Thing???
>
>Anyway, all of this is speculative, because until now, The hack saw
>and lathe back grinder have been the tools used. It would be very
>good for me (fundamental) to have your ideas on it
>
>Kind regards and happy car-making!
>
>D.R.

Pat Patterson
Abbotsford, BC, Canada

2001 PT Cruiser
83 450 Honda Nighthawk
78 F350 460/C6 on propane
71 Bronco 302/C4/D20 D44/9"

Some people try to turn back their odometers. Not me, I want people
to know "why" I look this way. I've traveled a long way and some of
the roads weren't paved.

"If you can't take the heat, don't tickle the dragon."





[Non-text portions of this message have been removed]

---Escoa, the tubing, unless known with its SAE #, and even then being correct,
is layered, Austinite, Pearlite, etc, depending on the anealing, hardining
proesses employed.
   This graining will wick, thru capilary action, the braze filler.( Some
fluxes willmake it more pronounced than others), allong the grain setting up
failure in time thru the different expansion, contraction cycles.
    That said, have Brazed joints I made 35 years ago still looking good.
     Also have souldered joints still working.
     If we are talking about BNiCr then the 1850-2050 needed,kinda says, gas
weld it.
     Yes, the lower heat spread of Mig or Tig are prefered.
  Hope this
helps.                                     \
                                        \
       George 1129

From: EskoA <eskoa@...>
To: locost@yahoogroups.com
Sent: Monday, August 22, 2011 7:24:14 PM
Subject: RE: [locost] Question on Brazing


 
Pat,

Why would you not braze the frame together? All the Lotus 7 frames were
brazed and the non-metric Caterham frames are still brazed, so what gives?

Esko

From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
Pat Patterson
Sent: Monday, August 22, 2011 7:41 AM
To: locost@yahoogroups.com
Subject: Re: [locost] Question on Brazing

Where are you from? English is obviously not your language. I'm
hoping something is being lost in translation because I wouldn't
braze any of the joints. I'd be willing to weld them with
oxyacetylene but not braze.

Knowing your language and location might help someone close to you
translate and or help with welding.

At 07:03 PM 8/20/2011, you wrote:
>
>
>Hello Locost/Lotus builders! I've been reading this group during
>some years, and finally, as I've started cutting the tubes, getting
>all the inferior rails (using pat prince scans as the reference and
>Autocad for neatness) cut and straight for welding, I would like to
>have your advice in the joining technique. The thing is; I have an
>oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
>worth the effort to get the tubes into a shop to Tack weld them with
>MIG, then braze it with nickel bronze at home???? mainly, i'm
>concerned with the lack of proper jigs for brazing it from the
>start, keeping it straight during the brazing (Being a complete
>practical novice on it, some literature already seen) so, i thought
>of the MIG for tacking all, four corners by tube prior to brazing.
>
>Another concern is the time involved, I am doing this project as
>slow as my work allows it, so if I have the chassis at home, tacked,
>it could be brazed little by little.
>
>And third!! this would be in the brazing alternative. Three tubes,
>two of them joint by their extremes, the third standing in it
>extreme, half of the inch on one tube, half on the other. Should I
>braze First the two underling tubes, THEN the standing one?. Should
>I Tack the three together, then braze the whole "Tee" Thing???
>
>Anyway, all of this is speculative, because until now, The hack saw
>and lathe back grinder have been the tools used. It would be very
>good for me (fundamental) to have your ideas on it
>
>Kind regards and happy car-making!
>
>D.R.

Pat Patterson
Abbotsford, BC, Canada

2001 PT Cruiser
83 450 Honda Nighthawk
78 F350 460/C6 on propane
71 Bronco 302/C4/D20 D44/9"

Some people try to turn back their odometers. Not me, I want people
to know "why" I look this way. I've traveled a long way and some of
the roads weren't paved.

"If you can't take the heat, don't tickle the dragon."

[Non-text portions of this message have been removed]




[Non-text portions of this message have been removed]

George:

Things have progressed since the days Gary, a local racer, built a Formula
Vee using an oxy-acetelene torch and coathangers for rod.  Pardon the pun,
but it hung together for many years of racing.

Good to see your still around, George.

I still have just a garage full of parts.  The local authority told me they
would never licence my Locost, so I quit working on it.  I have been
thinking about moving it home and starting work on it again.  Heck, I have
even thought of moving to Alberta where they are a little more open minded.

Ed Bratt
Regina, Saskatchewan.

----- Original Message -----
From: "George" <geo1129@...>
To: <locost@yahoogroups.com>
Sent: Monday, August 22, 2011 6:16 PM
Subject: Re: [locost] Question on Brazing


> ---Escoa, the tubing, unless known with its SAE #, and even then being
> correct, is layered, Austinite, Pearlite, etc, depending on the anealing,
> hardining proesses employed.
> This graining will wick, thru capilary action, the braze filler.( Some
> fluxes willmake it more pronounced than others), allong the grain setting
> up failure in time thru the different expansion, contraction cycles.
> That said, have Brazed joints I made 35 years ago still looking good.
> Also have souldered joints still working.
> If we are talking about BNiCr then the 1850-2050 needed,kinda says, gas
> weld it.
> Yes, the lower heat spread of Mig or Tig are prefered.
> Hope this helps. George 1129
>
> From: EskoA <eskoa@...>
> To: locost@yahoogroups.com
> Sent: Monday, August 22, 2011 7:24:14 PM
> Subject: RE: [locost] Question on Brazing
>
>
>
> Pat,
>
> Why would you not braze the frame together? All the Lotus 7 frames were
> brazed and the non-metric Caterham frames are still brazed, so what gives?
>
> Esko
>
> From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
> Pat Patterson
> Sent: Monday, August 22, 2011 7:41 AM
> To: locost@yahoogroups.com
> Subject: Re: [locost] Question on Brazing
>
> Where are you from? English is obviously not your language. I'm
> hoping something is being lost in translation because I wouldn't
> braze any of the joints. I'd be willing to weld them with
> oxyacetylene but not braze.
>
> Knowing your language and location might help someone close to you
> translate and or help with welding.
>
> At 07:03 PM 8/20/2011, you wrote:
>>
>>
>>Hello Locost/Lotus builders! I've been reading this group during
>>some years, and finally, as I've started cutting the tubes, getting
>>all the inferior rails (using pat prince scans as the reference and
>>Autocad for neatness) cut and straight for welding, I would like to
>>have your advice in the joining technique. The thing is; I have an
>>oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
>>worth the effort to get the tubes into a shop to Tack weld them with
>>MIG, then braze it with nickel bronze at home???? mainly, i'm
>>concerned with the lack of proper jigs for brazing it from the
>>start, keeping it straight during the brazing (Being a complete
>>practical novice on it, some literature already seen) so, i thought
>>of the MIG for tacking all, four corners by tube prior to brazing.
>>
>>Another concern is the time involved, I am doing this project as
>>slow as my work allows it, so if I have the chassis at home, tacked,
>>it could be brazed little by little.
>>
>>And third!! this would be in the brazing alternative. Three tubes,
>>two of them joint by their extremes, the third standing in it
>>extreme, half of the inch on one tube, half on the other. Should I
>>braze First the two underling tubes, THEN the standing one?. Should
>>I Tack the three together, then braze the whole "Tee" Thing???
>>
>>Anyway, all of this is speculative, because until now, The hack saw
>>and lathe back grinder have been the tools used. It would be very
>>good for me (fundamental) to have your ideas on it
>>
>>Kind regards and happy car-making!
>>
>>D.R.
>
> Pat Patterson
> Abbotsford, BC, Canada
>
> 2001 PT Cruiser
> 83 450 Honda Nighthawk
> 78 F350 460/C6 on propane
> 71 Bronco 302/C4/D20 D44/9"
>
> Some people try to turn back their odometers. Not me, I want people
> to know "why" I look this way. I've traveled a long way and some of
> the roads weren't paved.
>
> "If you can't take the heat, don't tickle the dragon."
>
> [Non-text portions of this message have been removed]
>
>
>
>
> [Non-text portions of this message have been removed]
>
>
>
> ------------------------------------
>
> Yahoo! Groups Links
>
>
>
>


--------------------------------------------------------------------------------



No virus found in this incoming message.
Checked by AVG - www.avg.com
Version: 8.5.449 / Virus Database: 271.1.1/3850 - Release Date: 08/22/11
06:35:00

Gut feeling. I'm a ticketed structural welder.
I've at least tried every process out there. I've
watched lots and lots of newb's weld with all the processes.

If you taught yourself on your locost and it
worked well, and from other pics and comments
your's has, I have huge respect and props to your
skill Sir. Brazing requires 3 different and
difficult things done to make it work. 1) your
fit up must be near perfect, 2) brazing requires
VERY careful heat control, 3) It can be a
difficult process to inspect well. Like micro
wire mig it's easy to have a bad joint look good.
Braze (brass and ???) has good adhesion but it's
other properties suck. So it makes a good glue
for very tight joints but if you have a gap where
your depending on the strength of the braze it's going to crack and fail.

Race cars, especially Mr. Chapman's Can't be
compared to a street vehicle. The original lotus
race cars were considered disposable. Any part
that made it farther than the victory lap was too
strong. After a race the cars are torn down and
every joint is re-inspected. This is still true
today in the upper racing classes. F1, NASCAR,
CART INDY etc. Hell even our pro buggy gets all
it's suspension and cage joints checked after a
race weekend. I keep looking till I find the
crack... there is always at least one.

I'm surprised that the current Caterham are still
brazed and would be very interested to find out
why. It just seems such a poor choice with what
else is available (to a first world car
manufacturer anyway). With a jig and a pile of
pre-cut tubes (how I would set up a shop to build
multiple frames). Using Mig I could have a frame
fully assembled and tacked by lunch and full weld
out by the end of the second day. And I'm slow.

Given the tools and exp he has available to him
I'd oxy fuel weld but not braze. A bad oxy fuel
weld looks like a bad weld, a badly brazed joint
can look nice. Professional pipe welders that do
it all day everyday still screw up every 100th
weld or so, it's important to be able to tell which weld that was.
As for coat hanger vs good wire... I've spent
some time recently around go-cart tracks. All
commercial go-carts are mig/tig today but the old
timers tell me that when they used to use oxy
fuel a coat hanger would crack less than a real
welding rod. My only personal exp with paid for
oxy fuel welding ( lots in class little after) is
making gas tanks for small engines. Brigs and
Stratton etc. The co. I worked for made small 3-5
hp gas powered water pumps. We cut the factory
gas tank in half and welded in an extension. I
found there too that old coat hanger wire with
the glue/varnish burned off lasted longer with
the high vibration than the real rods. The
hypothesis is the junk in the wire makes it more maliable.

Please no one take offence if that's how you did
it. In truth I'd like to know why you chose that
instead of oxy welding considering the same tools are used for each.


At 04:24 PM 8/22/2011, you wrote:
>
>
>Pat,
>
>Why would you not braze the frame together? All the Lotus 7 frames were
>brazed and the non-metric Caterham frames are still brazed, so what gives?
>
>Esko
>
>From:
><mailto:locost%40yahoogroups.com>locost@yahoogroups.com
>[mailto:locost@yahoogroups.com] On Behalf Of
>Pat Patterson
>Sent: Monday, August 22, 2011 7:41 AM
>To: <mailto:locost%40yahoogroups.com>locost@yahoogroups.com
>Subject: Re: [locost] Question on Brazing
>
>Where are you from? English is obviously not your language. I'm
>hoping something is being lost in translation because I wouldn't
>braze any of the joints. I'd be willing to weld them with
>oxyacetylene but not braze.
>
>Knowing your language and location might help someone close to you
>translate and or help with welding.
>
>At 07:03 PM 8/20/2011, you wrote:
> >
> >
> >Hello Locost/Lotus builders! I've been reading this group during
> >some years, and finally, as I've started cutting the tubes, getting
> >all the inferior rails (using pat prince scans as the reference and
> >Autocad for neatness) cut and straight for welding, I would like to
> >have your advice in the joining technique. The thing is; I have an
> >oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
> >worth the effort to get the tubes into a shop to Tack weld them with
> >MIG, then braze it with nickel bronze at home???? mainly, i'm
> >concerned with the lack of proper jigs for brazing it from the
> >start, keeping it straight during the brazing (Being a complete
> >practical novice on it, some literature already seen) so, i thought
> >of the MIG for tacking all, four corners by tube prior to brazing.
> >
> >Another concern is the time involved, I am doing this project as
> >slow as my work allows it, so if I have the chassis at home, tacked,
> >it could be brazed little by little.
> >
> >And third!! this would be in the brazing alternative. Three tubes,
> >two of them joint by their extremes, the third standing in it
> >extreme, half of the inch on one tube, half on the other. Should I
> >braze First the two underling tubes, THEN the standing one?. Should
> >I Tack the three together, then braze the whole "Tee" Thing???
> >
> >Anyway, all of this is speculative, because until now, The hack saw
> >and lathe back grinder have been the tools used. It would be very
> >good for me (fundamental) to have your ideas on it
> >
> >Kind regards and happy car-making!
> >
> >D.R.
>
>Pat Patterson
>Abbotsford, BC, Canada
>
>2001 PT Cruiser
>83 450 Honda Nighthawk
>78 F350 460/C6 on propane
>71 Bronco 302/C4/D20 D44/9"
>
>Some people try to turn back their odometers. Not me, I want people
>to know "why" I look this way. I've traveled a long way and some of
>the roads weren't paved.
>
>"If you can't take the heat, don't tickle the dragon."
>
>[Non-text portions of this message have been removed]
>
>

Pat Patterson
Abbotsford, BC, Canada


2001 PT Cruiser
83 450 Honda Nighthawk
78 F350    460/C6 on propane
71 Bronco 302/C4/D20 D44/9"


Some people try to turn back their
odometers.  Not me, I want people to know "why" I
look this way.  I've traveled a long way and some of the roads weren't paved.

"If you can't take the heat, don't tickle the dragon."














[Non-text portions of this message have been removed]

At 07:38 PM 8/22/2011, you wrote:
>
>
>George:
>
>Things have progressed since the days Gary, a local racer, built a Formula
>Vee using an oxy-acetelene torch and coathangers for rod. Pardon the pun,
>but it hung together for many years of racing.
>
>Good to see your still around, George.
>
>I still have just a garage full of parts. The local authority told me they
>would never licence my Locost, so I quit working on it. I have been
>thinking about moving it home and starting work on it again. Heck, I have
>even thought of moving to Alberta where they are a little more open minded.
>
>Ed Bratt
>Regina, Saskatchewan.


You're in Canada why the hell won't they licence it? Bah just head
west till you get to the mountains, I'll open the gates and let you
into gods country myself ;o) But seriously Build it, take it left or
right, register, insure, bring it home. treat as any other licensed
vehicle moved into the province.


Pat Patterson
Abbotsford, BC, Canada


2001 PT Cruiser
83 450 Honda Nighthawk
78 F350    460/C6 on propane
71 Bronco 302/C4/D20 D44/9"


Some people try to turn back their odometers.  Not me, I want people
to know "why" I look this way.  I've traveled a long way and some of
the roads weren't paved.

"If you can't take the heat, don't tickle the dragon."

Pat:

The authorities at Sask Government Insurance like to grab every bit of power
they can.  Some rumours suggest they are compensating for tiny weenies;
Others say it is because they grew up as cronic bed wetters.  They are
compensating for something, but I really do not know what.  But it makes
them feel big and important to say "NO" real loud.

I have just about a complete unassembled Locost, and it is time I did get
back to it.

There is even a choice of engines in my garage.  I have a 4AGE, and also a
3AC single cam toyota engine, and a BMC 1275 MG Midget engine and
transmission.

I have lost count of the years it has been sitting.  My son moved to
Victoria to get educated, and it would be a wonderful experience to drive it
through the mountains.  I have driven a Mini through the mountains, slow
going up, but an absolute thrill coming down.

Got to finish it.

Ed Bratt
Regina, Sask


----- Original Message -----
From: "Pat Patterson" <pat@...>
To: <locost@yahoogroups.com>
Sent: Monday, August 22, 2011 8:52 PM
Subject: Re: [locost] Question on Brazing


> At 07:38 PM 8/22/2011, you wrote:
>>
>>
>>George:
>>
>>Things have progressed since the days Gary, a local racer, built a Formula
>>Vee using an oxy-acetelene torch and coathangers for rod. Pardon the pun,
>>but it hung together for many years of racing.
>>
>>Good to see your still around, George.
>>
>>I still have just a garage full of parts. The local authority told me they
>>would never licence my Locost, so I quit working on it. I have been
>>thinking about moving it home and starting work on it again. Heck, I have
>>even thought of moving to Alberta where they are a little more open
>>minded.
>>
>>Ed Bratt
>>Regina, Saskatchewan.
>
>
> You're in Canada why the hell won't they licence it? Bah just head
> west till you get to the mountains, I'll open the gates and let you
> into gods country myself ;o) But seriously Build it, take it left or
> right, register, insure, bring it home. treat as any other licensed
> vehicle moved into the province.
>
>
> Pat Patterson
> Abbotsford, BC, Canada
>
>
> 2001 PT Cruiser
> 83 450 Honda Nighthawk
> 78 F350    460/C6 on propane
> 71 Bronco 302/C4/D20 D44/9"
>
>
> Some people try to turn back their odometers.  Not me, I want people
> to know "why" I look this way.  I've traveled a long way and some of
> the roads weren't paved.
>
> "If you can't take the heat, don't tickle the dragon."
>
>
>
>
>
>
>
>
>
>
>
>
>
>
>
> ------------------------------------
>
> Yahoo! Groups Links
>
>
>


--------------------------------------------------------------------------------



No virus found in this incoming message.
Checked by AVG - www.avg.com
Version: 8.5.449 / Virus Database: 271.1.1/3850 - Release Date: 08/22/11
06:35:00

---Yup, dem revnuers taint gots me yet.
  Not really progressed for what we do, Learned brazing back when we had to use
powder for flux and graduated to the dip in flux, braze, dip, braze as well as
scratching the work and keep a puddle going.
  Have Millers as well as a Hobart SP250 now-a-days, but sometimes miss the
older-slower ways.
  Ed, as a Canadian,  Build it, there is allways a way to legalize it later.
You have to remember, there is a law agaist everything, But, its all at the
discression of the investagator.
   Sorry to hear an admitance of  THEY won after your travelling such
distance in your quest for the right stuff as well as your helping of others in
their quests as well as you could.
    Good to hear your getting back at it.
   Assembling parts myself for the next build. Sold my 1 st build to a man in
Barrie. He seen it in front of my place, left his family at Timmy's, came back
with a fist-full of cash, I could'nt say no.
    Second build still going strong and owner will not sell.
     Third, was at wrecker on Sat. and found another rad as Chevette was
too small and leaking too much to patch. Should be back on road soon.
     All 3 had various legal issues for road use.
   Mine, kept insisting it was a dune-buggy for off-road use ammong other
issues.
   Will not go into insurance probs. But, its doable with perserverance.
 Hope this
helps.                                     \
                                        \
                  Geo1129

From: ed <bratt@...>
To: locost@yahoogroups.com
Sent: Monday, August 22, 2011 10:38:13 PM
Subject: Re: [locost] Question on Brazing


 
George:

Things have progressed since the days Gary, a local racer, built a Formula
Vee using an oxy-acetelene torch and coathangers for rod. Pardon the pun,
but it hung together for many years of racing.

Good to see your still around, George.

I still have just a garage full of parts. The local authority told me they
would never licence my Locost, so I quit working on it. I have been
thinking about moving it home and starting work on it again. Heck, I have
even thought of moving to Alberta where they are a little more open minded.

Ed Bratt
Regina, Saskatchewan.

----- Original Message -----
From: "George" <geo1129@...>
To: <locost@yahoogroups.com>
Sent: Monday, August 22, 2011 6:16 PM
Subject: Re: [locost] Question on Brazing

> ---Escoa, the tubing, unless known with its SAE #, and even then being
> correct, is layered, Austinite, Pearlite, etc, depending on the anealing,
> hardining proesses employed.
> This graining will wick, thru capilary action, the braze filler.( Some
> fluxes willmake it more pronounced than others), allong the grain setting
> up failure in time thru the different expansion, contraction cycles.
> That said, have Brazed joints I made 35 years ago still looking good.
> Also have souldered joints still working.
> If we are talking about BNiCr then the 1850-2050 needed,kinda says, gas
> weld it.
> Yes, the lower heat spread of Mig or Tig are prefered.
> Hope this helps. George 1129
>
> From: EskoA <eskoa@...>
> To: locost@yahoogroups.com
> Sent: Monday, August 22, 2011 7:24:14 PM
> Subject: RE: [locost] Question on Brazing
>
>
>
> Pat,
>
> Why would you not braze the frame together? All the Lotus 7 frames were
> brazed and the non-metric Caterham frames are still brazed, so what gives?
>
> Esko
>
> From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
> Pat Patterson
> Sent: Monday, August 22, 2011 7:41 AM
> To: locost@yahoogroups.com
> Subject: Re: [locost] Question on Brazing
>
> Where are you from? English is obviously not your language. I'm
> hoping something is being lost in translation because I wouldn't
> braze any of the joints. I'd be willing to weld them with
> oxyacetylene but not braze.
>
> Knowing your language and location might help someone close to you
> translate and or help with welding.
>
> At 07:03 PM 8/20/2011, you wrote:
>>
>>
>>Hello Locost/Lotus builders! I've been reading this group during
>>some years, and finally, as I've started cutting the tubes, getting
>>all the inferior rails (using pat prince scans as the reference and
>>Autocad for neatness) cut and straight for welding, I would like to
>>have your advice in the joining technique. The thing is; I have an
>>oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
>>worth the effort to get the tubes into a shop to Tack weld them with
>>MIG, then braze it with nickel bronze at home???? mainly, i'm
>>concerned with the lack of proper jigs for brazing it from the
>>start, keeping it straight during the brazing (Being a complete
>>practical novice on it, some literature already seen) so, i thought
>>of the MIG for tacking all, four corners by tube prior to brazing.
>>
>>Another concern is the time involved, I am doing this project as
>>slow as my work allows it, so if I have the chassis at home, tacked,
>>it could be brazed little by little.
>>
>>And third!! this would be in the brazing alternative. Three tubes,
>>two of them joint by their extremes, the third standing in it
>>extreme, half of the inch on one tube, half on the other. Should I
>>braze First the two underling tubes, THEN the standing one?. Should
>>I Tack the three together, then braze the whole "Tee" Thing???
>>
>>Anyway, all of this is speculative, because until now, The hack saw
>>and lathe back grinder have been the tools used. It would be very
>>good for me (fundamental) to have your ideas on it
>>
>>Kind regards and happy car-making!
>>
>>D.R.
>
> Pat Patterson
> Abbotsford, BC, Canada
>
> 2001 PT Cruiser
> 83 450 Honda Nighthawk
> 78 F350 460/C6 on propane
> 71 Bronco 302/C4/D20 D44/9"
>
> Some people try to turn back their odometers. Not me, I want people
> to know "why" I look this way. I've traveled a long way and some of
> the roads weren't paved.
>
> "If you can't take the heat, don't tickle the dragon."
>
> [Non-text portions of this message have been removed]
>
>
>
>
> [Non-text portions of this message have been removed]
>
>
>
> ------------------------------------
>
> Yahoo! Groups Links
>
>
>
>

----------------------------------------------------------

No virus found in this incoming message.
Checked by AVG - www.avg.com
Version: 8.5.449 / Virus Database: 271.1.1/3850 - Release Date: 08/22/11
06:35:00




[Non-text portions of this message have been removed]

I MIGed my locost frame, because it was designed to be MIGed, I brazed my Lotus
23 frame because it was designed to be brazed. If I were to build a true seven
replica, I would braze it with the good stuff, Nickel bronze.
The joint designs are quite different, Brazing requires more surface area,
plenty of round tube to create good fillets, no butt joints and often tubes bent
rather than 2 pieces used . The locost is mainly square to square tube joints
and plenty of butt joints, so no good for brazing.
Brazing aparently dosn't change the structure of the steel to the degree fusion
welding does, therefore retains strength and dosn't put in as much heat so
reduces heat distortion on thin guage steel structures. This is contrary to
anyone selling  MIG welders and trained on them, but after MIGing a locost
frame, and Brazing a lotus 23 frame, I tend to believe it. There was minimal
distortion and heat build up on my 23 chassis. It was also pleasurable and
relaxing to weld.
MIG is faster thou and TIG is better than both of the others.

Patrick




   ----- Original Message -----
   From: EskoA
   To: locost@yahoogroups.com
   Sent: Tuesday, August 23, 2011 11:24 AM
   Subject: RE: [locost] Question on Brazing



   Pat,

   Why would you not braze the frame together? All the Lotus 7 frames were
   brazed and the non-metric Caterham frames are still brazed, so what gives?

   Esko

   From: locost@yahoogroups.com [mailto:locost@yahoogroups.com] On Behalf Of
   Pat Patterson
   Sent: Monday, August 22, 2011 7:41 AM
   To: locost@yahoogroups.com
   Subject: Re: [locost] Question on Brazing

   Where are you from? English is obviously not your language. I'm
   hoping something is being lost in translation because I wouldn't
   braze any of the joints. I'd be willing to weld them with
   oxyacetylene but not braze.

   Knowing your language and location might help someone close to you
   translate and or help with welding.

   At 07:03 PM 8/20/2011, you wrote:
   >
   >
   >Hello Locost/Lotus builders! I've been reading this group during
   >some years, and finally, as I've started cutting the tubes, getting
   >all the inferior rails (using pat prince scans as the reference and
   >Autocad for neatness) cut and straight for welding, I would like to
   >have your advice in the joining technique. The thing is; I have an
   >oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
   >worth the effort to get the tubes into a shop to Tack weld them with
   >MIG, then braze it with nickel bronze at home???? mainly, i'm
   >concerned with the lack of proper jigs for brazing it from the
   >start, keeping it straight during the brazing (Being a complete
   >practical novice on it, some literature already seen) so, i thought
   >of the MIG for tacking all, four corners by tube prior to brazing.
   >
   >Another concern is the time involved, I am doing this project as
   >slow as my work allows it, so if I have the chassis at home, tacked,
   >it could be brazed little by little.
   >
   >And third!! this would be in the brazing alternative. Three tubes,
   >two of them joint by their extremes, the third standing in it
   >extreme, half of the inch on one tube, half on the other. Should I
   >braze First the two underling tubes, THEN the standing one?. Should
   >I Tack the three together, then braze the whole "Tee" Thing???
   >
   >Anyway, all of this is speculative, because until now, The hack saw
   >and lathe back grinder have been the tools used. It would be very
   >good for me (fundamental) to have your ideas on it
   >
   >Kind regards and happy car-making!
   >
   >D.R.

   Pat Patterson
   Abbotsford, BC, Canada

   2001 PT Cruiser
   83 450 Honda Nighthawk
   78 F350 460/C6 on propane
   71 Bronco 302/C4/D20 D44/9"

   Some people try to turn back their odometers. Not me, I want people
   to know "why" I look this way. I've traveled a long way and some of
   the roads weren't paved.

   "If you can't take the heat, don't tickle the dragon."

   [Non-text portions of this message have been removed]





[Non-text portions of this message have been removed]

First, Never use brazing for structural members. It is not strong enough. Braze
sheet metal panels but not frames. I have own several welders, and you get what
you pay for. If 220 is out of the question and you are using 120 wall, you
should be able to find a 120 volt welder capable of welding 120 wall.

When using square or rectangle tube, I have found the best way to 2 pieces with
out a jig is to use internal gussets. The gusset acts as your jig. Use a rosset
weld to hold the gusset in place. There will be minimal warping due to heat
expansion, and you can weld with more that 100% penetration. You will not find a
stronger weld anywhere. And you can grind it flush and still have a +100%
penetration weld.

Your betting your life on this frame, spend the money and get a gas shielded
MIG.

--- In locost@yahoogroups.com, "Daniel" <drichardson_ve@...> wrote:
>
> Hello Locost/Lotus builders! I've been reading this group during some years,
and finally, as I've started cutting the tubes, getting all the inferior rails
(using pat prince scans as the reference and Autocad for neatness) cut and
straight for welding, I would like to have your advice in the joining technique.
The thing is; I have an oxyacetilene torch, and no MIG, nor TIG, no 220v either.
Does it worth the effort to get the tubes into a shop to Tack weld them with
MIG, then braze it with nickel bronze at home???? mainly, i'm concerned with the
lack of proper jigs for brazing it from the start, keeping it straight during
the brazing (Being a complete practical novice on it, some literature already
seen) so, i thought of the MIG for tacking all, four corners by tube prior to
brazing.
>
> Another concern is the time involved, I am doing this project as slow as my
work allows it, so if I have the chassis at home, tacked, it could be brazed
little by little.
>
> And third!! this would be in the brazing alternative. Three tubes, two of them
joint by their extremes, the third standing in it extreme, half of the inch on
one tube, half on the other. Should I braze First the two underling tubes, THEN
the standing one?. Should I Tack the three together, then braze the whole "Tee"
Thing???
>
> Anyway, all of this is speculative, because until now, The hack saw and lathe
back grinder have been the tools used. It would be very good for me
(fundamental) to have your ideas on it
>
> Kind regards and happy car-making!
>
> D.R.
>

I wish you people would learn the difference between brazing and bronze
welding. This has been talked about on many forums and is easily
searched.  David (bronze weldor)

Hello Pat, Thank you for your answer. My language is spanish, I'm a musician
from Venezuela, and some years ago, while studying abroad, I saw a Seven (I'm
not sure wether a locost or lotus), back in that time I was thrilled by the
morgan 3 wheeler, and I hoped to make a Jzr style replica when I was home again.
Then, that very day I got in love with that nameless little car.

After finishing my studies and returning home with my wife pregnant, we bought a
Renault Fuego wich is our daily transport. But the seven has been a very wanted
project for me, and finally, I started cutting the tubes with a cad design wich
follows the outer lines from the pat prince plan, with a little more
triangulation for strenghtening the chassis. In fact, my brother is also doing
one for him, so, the work and tools costs are shared.

We plan to use a Fiat Twin Cam 1600 engine, With Honda CBR Carbs, Ford Sierra
Gearbox and transmission, Front Chevette Uprights, Rear Chris Gibbs fabricated
uprights. By reading the answers to this post, and after a call to the local
welding supplies store, (No nickel bronze rods), Perhaps I will use oxy fusion
welding, Perhaps MIG (paying a shop for it), It will depend on practicality,
here in my city.

The bronze nickel idea came from the knowledge that Arch Motors used that for
making the caterham chassis, now is a different story with Robotic MIG at Cage,
but I see that is a little bit difficult to get the proper materials to make it
that way. (I understand the technique isn't capillary brazing, so the gaps don't
need to be so precise as the filet or bronce ally is the tensile support) But,
to be honest, it seems more realistic to use steel rods, wich are far more
common, and fusion welding. I think a little tip for the torch will help.


kind regards from the Venezuelan Andes :)

Daniel Richardson

--- In locost@yahoogroups.com, Pat Patterson <pat@...> wrote:
>
> Where are you from? English is obviously not your language. I'm
> hoping something is being lost in translation because I wouldn't
> braze any of the joints. I'd be willing to weld them with
> oxyacetylene but not braze.
>
> Knowing your language and location might help someone close to you
> translate and or help with welding.
>
> At 07:03 PM 8/20/2011, you wrote:
> >
> >
> >Hello Locost/Lotus builders! I've been reading this group during
> >some years, and finally, as I've started cutting the tubes, getting
> >all the inferior rails (using pat prince scans as the reference and
> >Autocad for neatness) cut and straight for welding, I would like to
> >have your advice in the joining technique. The thing is; I have an
> >oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
> >worth the effort to get the tubes into a shop to Tack weld them with
> >MIG, then braze it with nickel bronze at home???? mainly, i'm
> >concerned with the lack of proper jigs for brazing it from the
> >start, keeping it straight during the brazing (Being a complete
> >practical novice on it, some literature already seen) so, i thought
> >of the MIG for tacking all, four corners by tube prior to brazing.
> >
> >Another concern is the time involved, I am doing this project as
> >slow as my work allows it, so if I have the chassis at home, tacked,
> >it could be brazed little by little.
> >
> >And third!! this would be in the brazing alternative. Three tubes,
> >two of them joint by their extremes, the third standing in it
> >extreme, half of the inch on one tube, half on the other. Should I
> >braze First the two underling tubes, THEN the standing one?. Should
> >I Tack the three together, then braze the whole "Tee" Thing???
> >
> >Anyway, all of this is speculative, because until now, The hack saw
> >and lathe back grinder have been the tools used. It would be very
> >good for me (fundamental) to have your ideas on it
> >
> >Kind regards and happy car-making!
> >
> >D.R.
>
> Pat Patterson
> Abbotsford, BC, Canada
>
>
> 2001 PT Cruiser
> 83 450 Honda Nighthawk
> 78 F350    460/C6 on propane
> 71 Bronco 302/C4/D20 D44/9"
>
>
> Some people try to turn back their odometers.  Not me, I want people
> to know "why" I look this way.  I've traveled a long way and some of
> the roads weren't paved.
>
> "If you can't take the heat, don't tickle the dragon."
>

Dave don't knock it this is the first proper question on this forum in months. I
remember back in the day there were dozens every day with people all over the
world helping each other build their car.

Dougie

Sent from my iPhone

On 23 Aug 2011, at 21:28, "David Dahl" <dfdahl@...> wrote:

> I wish you people would learn the difference between brazing and bronze
> welding. This has been talked about on many forums and is easily
> searched. David (bronze weldor)
>
>
>
> Click here to report this email as spam.
>


This message has been scanned for malware by SurfControl plc.
www.surfcontrol.com


[Non-text portions of this message have been removed]

Rick, thank you very much for this information, I agree that using gas is much
more precise and versatile than MIG, certainly the budget IS an important
concern, because my country do not make MIG or TIG equipment, so we have to
import it, and even the Chinese ones sometimes are unproportionally expensive.
We already bought The Oxy torch, regulators and nozzles (cutting attachment
included), for no much money, so, in that direction we have already most of what
we need. I remember reading a document from DSK wich speaks very good the
virtues of welding with gas a seven chassis, so, why not?

Of course, before that, practice, practice practice...

One thing I would like to know is, how would you tack two tubes with that? can I
do it on the MDF table??? or it will burn by the moment I finish tacking the
first corner of the tubes? I think of the inferior rails, to make them straight
against the table, 4 tacks and after checking all, weld it on the air.

kind regards

Daniel




--- In locost@yahoogroups.com, Richard Girard <jindoguy@...> wrote:
>
> Daniel, If you have oxy acetylene you don't need anything else. You will
> need 00, 0, 1, and 2 size torches to cover all the thicknesses of tubing and
> tabs. Add a cutting torch for fast fabrication of suspension tabs and you
> have everything you need. It may take a little longer, but you can fit,
> tack, check alignment, and finish weld and you'll be fine. Add a rosebud
> torch, you also have the advantage of being able to do bending, which
> neither MIG nor TIG will give you.
> Brazing requires very precise fits, welding is much more lenient. Just use
> good quality welding rod, ER70S6 is very common. no scrap wire or hangers
> :-}, that will cause cracks down the road.
> There are many videos out there showing oxy acetylene welding of aircraft
> fuselages, engine mounts, and control surfaces, get one of those and
> practice, practice, practice. Make sample welds on some tube drops, cut
> through them at a right angle and take those to a welder when you think you
> are skilled enough and ready to start you chassis. He will be able to give
> you an honest appraisal or your  skill.
> Almost every aircraft built during World War II had steel parts that
> were oxy acetylene welded. From the Spitfire to the Super Fortress, they had
> major structural weldments that were oxy acetylene welded. You will find you
> have more control of weld size and a much easier time getting into tight
> corners than with a MIG.
> Good luck.
>
> Rick Girard
>
>
> On Sat, Aug 20, 2011 at 9:03 PM, Daniel <drichardson_ve@...> wrote:
>
> > **
> >
> >
> > Hello Locost/Lotus builders! I've been reading this group during some
> > years, and finally, as I've started cutting the tubes, getting all the
> > inferior rails (using pat prince scans as the reference and Autocad for
> > neatness) cut and straight for welding, I would like to have your advice in
> > the joining technique. The thing is; I have an oxyacetilene torch, and no
> > MIG, nor TIG, no 220v either. Does it worth the effort to get the tubes into
> > a shop to Tack weld them with MIG, then braze it with nickel bronze at
> > home???? mainly, i'm concerned with the lack of proper jigs for brazing it
> > from the start, keeping it straight during the brazing (Being a complete
> > practical novice on it, some literature already seen) so, i thought of the
> > MIG for tacking all, four corners by tube prior to brazing.
> >
> > Another concern is the time involved, I am doing this project as slow as my
> > work allows it, so if I have the chassis at home, tacked, it could be brazed
> > little by little.
> >
> > And third!! this would be in the brazing alternative. Three tubes, two of
> > them joint by their extremes, the third standing in it extreme, half of the
> > inch on one tube, half on the other. Should I braze First the two underling
> > tubes, THEN the standing one?. Should I Tack the three together, then braze
> > the whole "Tee" Thing???
> >
> > Anyway, all of this is speculative, because until now, The hack saw and
> > lathe back grinder have been the tools used. It would be very good for me
> > (fundamental) to have your ideas on it
> >
> > Kind regards and happy car-making!
> >
> > D.R.
> >
> >
> >
>
>
> [Non-text portions of this message have been removed]
>

Mark, thanks for the gusset idea, certainly it should do the job and get a sound
joint! to think about...

Daniel

--- In locost@yahoogroups.com, "Mark" <mxwmxw@...> wrote:
>
> First, Never use brazing for structural members. It is not strong enough.
Braze sheet metal panels but not frames. I have own several welders, and you get
what you pay for. If 220 is out of the question and you are using 120 wall, you
should be able to find a 120 volt welder capable of welding 120 wall.
>
> When using square or rectangle tube, I have found the best way to 2 pieces
with out a jig is to use internal gussets. The gusset acts as your jig. Use a
rosset weld to hold the gusset in place. There will be minimal warping due to
heat expansion, and you can weld with more that 100% penetration. You will not
find a stronger weld anywhere. And you can grind it flush and still have a +100%
penetration weld.
>
> Your betting your life on this frame, spend the money and get a gas shielded
MIG.
>
> --- In locost@yahoogroups.com, "Daniel" <drichardson_ve@> wrote:
> >
> > Hello Locost/Lotus builders! I've been reading this group during some years,
and finally, as I've started cutting the tubes, getting all the inferior rails
(using pat prince scans as the reference and Autocad for neatness) cut and
straight for welding, I would like to have your advice in the joining technique.
The thing is; I have an oxyacetilene torch, and no MIG, nor TIG, no 220v either.
Does it worth the effort to get the tubes into a shop to Tack weld them with
MIG, then braze it with nickel bronze at home???? mainly, i'm concerned with the
lack of proper jigs for brazing it from the start, keeping it straight during
the brazing (Being a complete practical novice on it, some literature already
seen) so, i thought of the MIG for tacking all, four corners by tube prior to
brazing.
> >
> > Another concern is the time involved, I am doing this project as slow as my
work allows it, so if I have the chassis at home, tacked, it could be brazed
little by little.
> >
> > And third!! this would be in the brazing alternative. Three tubes, two of
them joint by their extremes, the third standing in it extreme, half of the inch
on one tube, half on the other. Should I braze First the two underling tubes,
THEN the standing one?. Should I Tack the three together, then braze the whole
"Tee" Thing???
> >
> > Anyway, all of this is speculative, because until now, The hack saw and
lathe back grinder have been the tools used. It would be very good for me
(fundamental) to have your ideas on it
> >
> > Kind regards and happy car-making!
> >
> > D.R.
> >
>

LinkedIn
------------




I'd like to add you to my professional network on LinkedIn.

- Robert

Robert Campbell
System/Network Controller at Safran Morpho
Amsterdam Area, Netherlands

Confirm that you know Robert Campbell
https://www.linkedin.com/e/pghvlj-grp8ekj8-22/isd/3954604059/QVYNa7tC/



--
(c) 2011, LinkedIn Corporation

[Non-text portions of this message have been removed]

Hi Daniel

The nickel bronze braze rods create a joint that is actually stronger
than the steel. As far as I have read there has few if any braze
joint failure on the 7's that were brazed including racing ones. You
see reports of the tubes rusting out etc but not the joints. And that
is after 20-30 years on the road or on the track. The problems with
brazing are making sure you have a good fit on the tube joint, clean
surfaces, and if your local authorities will let it be used.  The
reason it has fallen out of favour is not that it is weaker but that
it takes longer to complete a joint and the fit is a bit more picky.
MIG is just faster so for a shop where time is money they went with
faster systems. Nickel bronze is still used quite a lot in aerospace
products that require high reliability and strength. If you are not
comfortable gas welding then it still is a excellent alternative.

You could tack with your oxy setup.  Or you can just use a bunch of C
clamps or welding magnets. Tack welds are not that strong so tacking
it one place and transporting it runs the risk of popping some of
those tacks loose.  On your jig the trick to not burning the wood
under the joints is simple not to have anything under them. Basically
you cut holes under where the joint is.
Hold the tubes down either using clamps if you have a bunch of what
most people do is blocks of wood along side the tubes screwed to the
jig. If you follow the book and do the bottom rail then the top. Then
you can use the upright tubes and C clamps to self jig that point of
the assembly. Once you have tubes in at least the four corners you
can just place and braze in the rest with out any thing but a clamp.
That is probably harder to explain here than it is to do ;-]

With the Oxy rig you can just weld it with the torch. The nice thing
about this is once you have your hand and eye working your welds will
be strong and should look very close to a tig welded seam in
appearance.  Either of those ways would get you a very serviceable
frame. They require a bit more skill than a mig but a few hours of
practice or better a few lessons or supervision from an experienced
welder and you should be ok.

Dave


At 07:32 PM 22/08/2011, you wrote:
>First, Never use brazing for structural members. It is not strong
>enough. Braze sheet metal panels but not frames. I have own several
>welders, and you get what you pay for. If 220 is out of the question
>and you are using 120 wall, you should be able to find a 120 volt
>welder capable of welding 120 wall.
>
>When using square or rectangle tube, I have found the best way to 2
>pieces with out a jig is to use internal gussets. The gusset acts as
>your jig. Use a rosset weld to hold the gusset in place. There will
>be minimal warping due to heat expansion, and you can weld with more
>that 100% penetration. You will not find a stronger weld anywhere.
>And you can grind it flush and still have a +100% penetration weld.
>
>Your betting your life on this frame, spend the money and get a gas
>shielded MIG.
>
>--- In locost@yahoogroups.com, "Daniel" <drichardson_ve@...> wrote:
> >
> > Hello Locost/Lotus builders! I've been reading this group during
> some years, and finally, as I've started cutting the tubes, getting
> all the inferior rails (using pat prince scans as the reference and
> Autocad for neatness) cut and straight for welding, I would like to
> have your advice in the joining technique. The thing is; I have an
> oxyacetilene torch, and no MIG, nor TIG, no 220v either. Does it
> worth the effort to get the tubes into a shop to Tack weld them
> with MIG, then braze it with nickel bronze at home???? mainly, i'm
> concerned with the lack of proper jigs for brazing it from the
> start, keeping it straight during the brazing (Being a complete
> practical novice on it, some literature already seen) so, i thought
> of the MIG for tacking all, four corners by tube prior to brazing.
> >
> > Another concern is the time involved, I am doing this project as
> slow as my work allows it, so if I have the chassis at home,
> tacked, it could be brazed little by little.
> >
> > And third!! this would be in the brazing alternative. Three
> tubes, two of them joint by their extremes, the third standing in
> it extreme, half of the inch on one tube, half on the other. Should
> I braze First the two underling tubes, THEN the standing one?.
> Should I Tack the three together, then braze the whole "Tee" Thing???
> >
> > Anyway, all of this is speculative, because until now, The hack
> saw and lathe back grinder have been the tools used. It would be
> very good for me (fundamental) to have your ideas on it
> >
> > Kind regards and happy car-making!
> >
> > D.R.


[Non-text portions of this message have been removed]

Ed

I thought there have been a few Locosts on the road in Sask?
I wonder if you have the same problem I've seen in a few places
where the local inspector is just setting up his own little kingdom
and will interpret the rules as he/they see fit regardless of what
the rules say. Or is it just that bad now?

Dave
NBattford escapee



At 08:48 PM 22/08/2011, you wrote:
>Pat:
>
>The authorities at Sask Government Insurance like to grab every bit of power
>they can.  Some rumours suggest they are compensating for tiny weenies;
>Others say it is because they grew up as cronic bed wetters.  They are
>compensating for something, but I really do not know what.  But it makes
>them feel big and important to say "NO" real loud.
>
>I have just about a complete unassembled Locost, and it is time I did get
>back to it.
>
>There is even a choice of engines in my garage.  I have a 4AGE, and also a
>3AC single cam toyota engine, and a BMC 1275 MG Midget engine and
>transmission.
>
>I have lost count of the years it has been sitting.  My son moved to
>Victoria to get educated, and it would be a wonderful experience to drive it
>through the mountains.  I have driven a Mini through the mountains, slow
>going up, but an absolute thrill coming down.
>
>Got to finish it.
>
>Ed Bratt
>Regina, Sask
>
>
>----- Original Message -----
>From: "Pat Patterson" <pat@...>
>To: <locost@yahoogroups.com>
>Sent: Monday, August 22, 2011 8:52 PM
>Subject: Re: [locost] Question on Brazing
>
>
> > At 07:38 PM 8/22/2011, you wrote:
> >>
> >>
> >>George:
> >>
> >>Things have progressed since the days Gary, a local racer, built a Formula
> >>Vee using an oxy-acetelene torch and coathangers for rod. Pardon the pun,
> >>but it hung together for many years of racing.
> >>
> >>Good to see your still around, George.
> >>
> >>I still have just a garage full of parts. The local authority told me they
> >>would never licence my Locost, so I quit working on it. I have been
> >>thinking about moving it home and starting work on it again. Heck, I have
> >>even thought of moving to Alberta where they are a little more open
> >>minded.
> >>
> >>Ed Bratt
> >>Regina, Saskatchewan.
> >
> >
> > You're in Canada why the hell won't they licence it? Bah just head
> > west till you get to the mountains, I'll open the gates and let you
> > into gods country myself ;o) But seriously Build it, take it left or
> > right, register, insure, bring it home. treat as any other licensed
> > vehicle moved into the province.
> >
> >
> > Pat Patterson
> > Abbotsford, BC, Canada
> >
> >
> > 2001 PT Cruiser
> > 83 450 Honda Nighthawk
> > 78 F350    460/C6 on propane
> > 71 Bronco 302/C4/D20 D44/9"
> >
> >
> > Some people try to turn back their odometers.  Not me, I want people
> > to know "why" I look this way.  I've traveled a long way and some of
> > the roads weren't paved.
> >
> > "If you can't take the heat, don't tickle the dragon."
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> >
> > ------------------------------------
> >
> > Yahoo! Groups Links
> >
> >
> >
>
>
>-------------------------------------------------------------------------------\
-
>
>
>
>No virus found in this incoming message.
>Checked by AVG - www.avg.com
>Version: 8.5.449 / Virus Database: 271.1.1/3850 - Release Date: 08/22/11
>06:35:00
>
>
>
>------------------------------------
>
>Yahoo! Groups Links
>
>
>

[Non-text portions of this message have been removed]

On 8/23/2011 10:39 AM, Dougie Wells wrote:
>
> Dave don't knock it this is the first proper question on this forum in
> months. I remember back in the day there were dozens every day with
> people all over the world helping each other build their car.
>
> Dougie
>
> Sent from my iPhone
>
> On 23 Aug 2011, at 21:28, "David Dahl" <dfdahl@...
> <mailto:dfdahl%40telus.net>> wrote:
>
> > I wish you people would learn the difference between brazing and bronze
> > welding. This has been talked about on many forums and is easily
> > searched. David (bronze weldor)
> >
> >
> >
> > Click here to report this email as spam.
> >
>
> This message has been scanned for malware by SurfControl plc.
> www.surfcontrol.com
>
> [Non-text portions of this message have been removed]
>
>
> ------------------------------------------------------------------------
>
> No virus found in this message.
> Checked by AVG - www.avg.com <http://www.avg.com>
> Version: 10.0.1392 / Virus Database: 1520/3852 - Release Date: 08/23/11
>
Yea, sorry point taken    David


[Non-text portions of this message have been removed]

In MIG or Brazing, I find the best way to assembly is to tack and assemble as
much as possible. The rest of the assembly acts as the jig, keeping warping to a
minimum. One triangle keeps the next from warping, and so on.


If you can tack the entire thing, or largeassemblies with many piecestogether
before finishing any joint the structure will be your jig. when you finish the
joints.


If you must Braze, It's all about fit, fit, fit. You can not use brazing
material as filler. It will not be strong. Think tight joints like the joint on
a picture frame, and filled gaps will be weak.

Clean joints are important to, as with MIG, But make sure the joints are freshly
ground the same day you braze. No oil, dirt or rust, even if you can see the
rust. hit it with a flap disk.

 
Mark


________________________________
From: Daniel <drichardson_ve@...>
To: locost@yahoogroups.com
Sent: Tuesday, August 23, 2011 1:41 PM
Subject: [locost] Re: Question on Brazing


 
Rick, thank you very much for this information, I agree that using gas is much
more precise and versatile than MIG, certainly the budget IS an important
concern, because my country do not make MIG or TIG equipment, so we have to
import it, and even the Chinese ones sometimes are unproportionally expensive.
We already bought The Oxy torch, regulators and nozzles (cutting attachment
included), for no much money, so, in that direction we have already most of what
we need. I remember reading a document from DSK wich speaks very good the
virtues of welding with gas a seven chassis, so, why not?

Of course, before that, practice, practice practice...

One thing I would like to know is, how would you tack two tubes with that? can I
do it on the MDF table??? or it will burn by the moment I finish tacking the
first corner of the tubes? I think of the inferior rails, to make them straight
against the table, 4 tacks and after checking all, weld it on the air.

kind regards

Daniel

--- In locost@yahoogroups.com, Richard Girard <jindoguy@...> wrote:
>
> Daniel, If you have oxy acetylene you don't need anything else. You will
> need 00, 0, 1, and 2 size torches to cover all the thicknesses of tubing and
> tabs. Add a cutting torch for fast fabrication of suspension tabs and you
> have everything you need. It may take a little longer, but you can fit,
> tack, check alignment, and finish weld and you'll be fine. Add a rosebud
> torch, you also have the advantage of being able to do bending, which
> neither MIG nor TIG will give you.
> Brazing requires very precise fits, welding is much more lenient. Just use
> good quality welding rod, ER70S6 is very common. no scrap wire or hangers
> :-}, that will cause cracks down the road.
> There are many videos out there showing oxy acetylene welding of aircraft
> fuselages, engine mounts, and control surfaces, get one of those and
> practice, practice, practice. Make sample welds on some tube drops, cut
> through them at a right angle and take those to a welder when you think you
> are skilled enough and ready to start you chassis. He will be able to give
> you an honest appraisal or your  skill.
> Almost every aircraft built during World War II had steel parts that
> were oxy acetylene welded. From the Spitfire to the Super Fortress, they had
> major structural weldments that were oxy acetylene welded. You will find you
> have more control of weld size and a much easier time getting into tight
> corners than with a MIG.
> Good luck.
>
> Rick Girard
>
>
> On Sat, Aug 20, 2011 at 9:03 PM, Daniel <drichardson_ve@...> wrote:
>
> > **
> >
> >
> > Hello Locost/Lotus builders! I've been reading this group during some
> > years, and finally, as I've started cutting the tubes, getting all the
> > inferior rails (using pat prince scans as the reference and Autocad for
> > neatness) cut and straight for welding, I would like to have your advice in
> > the joining technique. The thing is; I have an oxyacetilene torch, and no
> > MIG, nor TIG, no 220v either. Does it worth the effort to get the tubes into
> > a shop to Tack weld them with MIG, then braze it with nickel bronze at
> > home???? mainly, i'm concerned with the lack of proper jigs for brazing it
> > from the start, keeping it straight during the brazing (Being a complete
> > practical novice on it, some literature already seen) so, i thought of the
> > MIG for tacking all, four corners by tube prior to brazing.
> >
> > Another concern is the time involved, I am doing this project as slow as my
> > work allows it, so if I have the chassis at home, tacked, it could be brazed
> > little by little.
> >
> > And third!! this would be in the brazing alternative. Three tubes, two of
> > them joint by their extremes, the third standing in it extreme, half of the
> > inch on one tube, half on the other. Should I braze First the two underling
> > tubes, THEN the standing one?. Should I Tack the three together, then braze
> > the whole "Tee" Thing???
> >
> > Anyway, all of this is speculative, because until now, The hack saw and
> > lathe back grinder have been the tools used. It would be very good for me
> > (fundamental) to have your ideas on it
> >
> > Kind regards and happy car-making!
> >
> > D.R.
> >
> >
> >
>
>
> [Non-text portions of this message have been removed]
>




[Non-text portions of this message have been removed]